Many thanks Pete! It never would have been possible to get something so incredibly nice on the first try without a whole lot of help.
More questions of course....
On the batch I just melted...
If I wanted to take the COE down to the 92-3 range to fit Fenton stuff, up to 96 to fit Spectrum, or even go completely nuts, kiss durability goodbye, and try taking it up around 102-4 to match Moretti, how would I go about it?
Would adding certain amounts of silica or soda be enough, or do the other things need to change on a percentage basis along with that?
What is the Corning Protocol?
I did melt it at 2200 after I got all the batch loaded and I'm pretty sure I would have screwed it up if I had tried at 2000.
__________________
Art is not a thing...it's a way.
|