Phosphates are not really dense glasses. They can and must be melted hot 2325F or higher. The junk will diminish is you melt hotter but it's almost always a problem in cooler melts.. Screen the phosphate materials. You can go up to 5% phosphate before you will hit a compatibility wall. Borax helps.
|