Phosphate Opal

After reading an older thread on Phosphate opals, I tried the following:

Quantities in pounds, except as shown

Sand 20
Soda Ash 4.6
Hydrted Lime 2
Zinc Oxide 1.2
Borax 3
Alumina Hydrate .6
Lithium Carb .6
Potassium Nitrate 73grams
Sodium Tripolyphosphate 2.8

After melting, I got a lot of crap on top but the glass underneath seems to be ok. I could have melted hotter, but wanted to take it easy because of glass in the other 2 pots.
My question is would a change to the time and temps of the melt help to reduce the junk on top, or is this just the way it is with this particular formula. The original purpose was to have a white that would be fairly dense, and have a viscosity close to the other colors that I make would have.
__________________
Rich
Reply With Quote
 


Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On
Forum Jump


All times are GMT -5. The time now is 10:50 AM.


All published comments within these message boards are the opinions of its contributor and does not represent
the opinion(s) of the owner(s) of this website. Please see the Terms of Use file for more details.

Books to Help Artists Avoid Online Scams: Top 10 Email Scams | Social Media Scams

Powered by vBulletin® Version 3.7.2
Copyright ©2000 - 2019, Jelsoft Enterprises Ltd.
CraftWEB.com. Opportunity Network. 2008. All Rights Reserved.